PART OF CATALOG
Quick change adaptors with safety clutch Size 2 | M8 | 8 x 6,2 | DIN 371
ER-Spannzange mit Kuhlkanalen ER16 | 426ECC | < 15µm | O 4
Hydraulic expansion chuck SK 50-20-82 DIN 69871 AD/B in wooden box
Application:
For mounting straight-shank tools acc. DIN 1835 form A+B+E and DIN 6535 form HA+HB+HE (larger than dia. 20 mm only with reduction sleeve).
Note:
l1 = max. clamping depth l2 = max. length adjustment range
Delivery:
With wrench
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
Sealing disc | OZ 25 DCONWS = 3,5
Claw jaws set (Pair) for AVQ-125 | AVL-125
Version:
Jaws with grip serrations und fine step for workpieces with max. edge radius 1 mm, clamping depth 2 mm
- For use on vises
- Simple, safe clamping of parallel raw and sawn parts
- Hydraulic or manual clamping
- Positive clamping due to penetration of the hardened claw tips
- High holding forces: increase by a factor of 3 to 5 compared to standard jaws
- Low material loss
- Shortened processing times and reduction of production and unit costs
Morse taper adaptor HSK 100 – 3 – 150
Application:
For mounting tools with Morse taper shank and tang according to DIN 228-1 form B.
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
Milling arbors for screw-in cutters SK 40 – M8 – 69 – LB50
Application:
For mounting screw-in cutters with thread.
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined