End mill holder Weldon HSK 63 – 18 – 80

102.00

Application:
For mounting straight-shank tools with lateral flat according to DIN 1835 form B (Weldon).


Delivery:
With clamping screw


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

Sealing disc | ER 32 DCONWS = 6,0

20.00

Application:
For sealing tools with internal cooling.


Note:
Sealing capacity up to 80 bar


Clamping range 0.5 mm (+0.1/?0.4)

Ring gauge “NO GO” M3 | 6g ISO-metric thread | DIN 13

36.00

Construction:

  • Hardened steel
  • ISO-Metric Thread
  • DIN 13
  • 6g

Delivery:
Calibration certificate

Morse taper adaptor SK 40 – 1 – 50

71.00

Application:
For clamping tools with Morse taper shank and thread according to DIN 228-1 form A.

With built-in tightening bolt


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

Quick change adaptors without safety clutch Size 2 | 16 x 12

24.00

Application:
For mounting taps. For right-hand and left-hand threads. Standard type without safety clutch.


Note:
Quick change adaptors without safety clutch can be interchanged, because only the shaft diameters and the squares must fit.

Milling arbors for screw-in cutters BT 40 – M12 – 102 – LB75

116.00

Application:
For mounting screw-in cutters with thread.


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 