Morse taper adaptor – form F1 F1 – 40 – MK4
ER-Precision collet ER32 | 470EP | < 5µm | O 4 - 3
ER-Collet chuck BT 30 – 1/10 – 70 | ER 16 | Mini
Application:
For mounting straight-shank tools in collets.
Delivery:
With balanced clamping nut
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
Precision collet set | radial run-out of < 3 µm ER 32 | 470 EHP | 15-part kit in wooden box
Application:
Metallic sealed for mounting straight-shank tools with coolant-through in collet chucks ISO 15488 (ex. DIN 6499).
Version:
Metallic sealed Collets for internal cooling (applicable up to 100 bar).
System concentricity and repetition accuracy 3 µm (3?D, maximum = 50 mm), in conjunction with KEMMLER Precision collet chuck ER".
Suitable for:
KEMMLER Precision collet chuck ER or standard collet chuck Spannfutter ISO 15488 (ex. DIN 6499).
Note:
Clamping range h6 (nominal size only).
Metallic sealed Collets for internal cooling (applicable up to 100 bar). In order to achieve an optimum sealing the tool must be clamped on the complete length of the ground drill of the collet.
End mill holder Weldon HSK63 – 12 – 100
Application:
For mounting straight-shank tools with lateral flat according to DIN 1835 form B (Weldon).
Delivery:
With clamping screw
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
End mill holder Weldon with cooling channels SK 40 – 14 – 50
Application:
For mounting straight-shank tools with lateral flat according to DIN 1835 form B (Weldon).
Delivery:
With clamping screw and O-ring
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
OZ-Collet chuck SK 50 – 2/25 – 70 | OZ 25
Application:
For mounting straight-shank tools in collets.
Delivery:
With ball bearing clamping nut
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined