ER-Collet chuck HSK 63 – 2/13 – 160 | ER 20
Application:
For mounting straight-shank tools in collets.
Delivery:
With balanced clamping nut
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
ER-Precision collet | stainless steel ER25 | 430ESP | < 5 µm | O 8,0 - 7,5
ER-Spannzange mit Kuhlkanalen ER40 | 472ECC | < 15µm | O 4
Boring holder for drills with indexable inserts | HSK 63 – 25 – 90
Application:
For mounting solid drills with cylindrical shank according to DIN 6595.
Note:
Contact surface precision grinded
Delivery:
With clamping screws
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
HSSE twist drill 135° 11,0 mm DIN 338 | TIN coating
End mill holder Weldon SK 50 – 10 – 200
Application:
For mounting straight-shank tools with lateral flat according to DIN 1835 form B (Weldon).
Delivery:
With clamping screw
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
End mill holder Whistle-Notch HSK 100 – 40 – 120
Application:
For mounting straight-shank tools and inclined flat according to DIN 1835 form E (Whistle Notch).
Delivery:
With clamping screw and axial adjustment bolt
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined