Quick change tapping chuck HSK 100 – M3-M14 – Gr.1
Application:
For the chucking of quick change adaptors for taps.
Note:
For machining centres with synchronous spindle.
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
Morse taper adaptor HSK 100 – 1 – 110
Application:
For clamping tools with Morse taper shank and thread according to DIN 228-1 form A.
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
Precision collet sets 470EP (ER32; 15 parts) in wooden box DIN 6499 B (ISO 15488 B)
End mill holder Weldon BT 40 – 14 – 100
Application:
For mounting straight-shank tools with lateral flat according to DIN 1835 form B (Weldon).
Delivery:
With clamping screw
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Taper angle tolerance < AT 3 according to DIN 2080
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
KPS-Collet chuck HSK 63 – 1/10 – 90 | KPS 10
Application:
For mounting straight-shank tools in collets. To use for high speed cutting and high precision milling.
Delivery:
With balanced clamping nut
- All holders are made of forged steel
- Specific, low warpage hardened
- Surface hardened HRC 58~60
- Hardening depth 0,8mm~0,9mm
- Surface roughness Ra < 0,4 µm
- Tensile strength in the core of min. 800 N/mm? after DIN
- All functional surfaces fine machined
Sealing disc | ER 40 DCONWS = 10,5
ER-Precision collet ER11 | 4008EP | < 5µm | O 3,0 - 2,5
FREE CONSULTATION
Have questions?
Leave a request
OUR PARTNERS