End mill holder Weldon HSK63 – 12 – 100

123.00

Application:
For mounting straight-shank tools with lateral flat according to DIN 1835 form B (Weldon).


Delivery:
With clamping screw


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

Solid carbide 4 flutes short 12mm 12,0 – 12 AlTiCrN coating

55.00

Application:
Coating: AlTiCrN, Excellent high-performance end mills, for processing material < 48HRC, for weldon shanks according to DIN 6535 HB.

ER-Precision collet chuck BT 40 – 2/20 – 150 | ER 32

128.00

Application:
For mounting straight-shank tools in 2 µm-collets.


Advantage:

  • Excellent concentricity in the system (chuck + collet + clamping nut)
  • 3 µm radial run-out with a 2 µm clamping nut, 6 µm radial run-out with a 5 µm clamping nut
  • Extremely strong holding force (increases the holding power by at least 60% compared to standard ER chuck)
  • Plain clamping nut without grooves for high speed machining

 

Combi shell mill holder BT 30 – 27 – 49

61.00

Application:
For mounting milling cutters with transverse or longitudinal groove.


Delivery:
With retaining screw, driving ring and feather key


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

Morse taper adaptor SK 30 – 3 – 80

47.00

Application:
For mounting tools with Morse taper shank and tang according to DIN 228-1 form B.


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

Zwischenhulse fur Steilkegel BT 50 – SK 50 – 120

168.00

Application:
For holding tapers according to DIN 69871, JIS B 6339 and DIN 2080.


Delivery:
Delivered with a built-in screw for shortened taper tools. Additional screw for DIN 2080 tools included.


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

Solid carbide 4 flutes short 2mm 2,0 – 6 AlTiCrN coating

15.00

Application:
Coating: AlTiCrN, Excellent high-performance end mills, for processing material < 48HRC, for weldon shanks according to DIN 6535 HB.

Shrink chuck 4,5° BT 40 – 10 – 90

140.00

Application:
For mounting tools with straight shanks.


Note:
Toolholders suitable for induction-, contact- and hot air shrink units. O 3, 4, 5 with h4-tolerance and O 6 – O 32 with h6-tolerance


For O 3, 4 and 5 mm only solid carbide tool shanks must be used!


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined