KPS-Collet chuck BT 30 – 1/10 – 60 | KPS 10

116.00

Application:
For mounting straight-shank tools in collets. To use for high speed cutting and high precision milling.


Delivery:
With balanced clamping nut


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

KPS-Collet chuck BT 30 – 1/10 – 90 | KPS 10

121.00

Application:
For mounting straight-shank tools in collets. To use for high speed cutting and high precision milling.


Delivery:
With balanced clamping nut


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

KPS-Collet chuck BT 30 – 4/16 – 60 | KPS 16

133.00

Application:
For mounting straight-shank tools in collets. To use for high speed cutting and high precision milling.


Delivery:
With balanced clamping nut


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

KPS-Collet chuck BT 30 – 4/16 – 90 | KPS 16

143.00

Application:
For mounting straight-shank tools in collets. To use for high speed cutting and high precision milling.


Delivery:
With balanced clamping nut


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined