End mill holder Weldon SK 40 – 40 – 120

118.00

Application:
For mounting straight-shank tools with lateral flat according to DIN 1835 form B (Weldon).


Delivery:
With clamping screw


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

Milling arbors for screw-in cutters BT 50 – M16 – 88 – LB50

132.00

Application:
For mounting screw-in cutters with thread.


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

End mill cutter 90° 32mm – 25mm Shank after DIN 1835B

221.00

  • For ISO Inserts APKT 1003... / APHX 1003...
  • With internal cooling
  • Nickel plated
  • Shank after DIN 1835B
  • Application in all materials
  • Delivery: without inserts

Ring gauge | 4,5mm ring gauge-accuracy DIN 2250

46.00

Note:
Construction: Hardened steel


Ring gauge accuracy according to DIN 2250

Delivery:
Calibration certificate

Morse taper adaptor – form F1 F1 – 50 – MK3

120.00

Application:
For mounting tools with Morse taper shank and tang according to DIN 228-1 form B.


Note:
With adjustable spray nozzles


KPS-Collet chuck BT 40 – 4/16 – 90 | KPS 16

138.00

Application:
For mounting straight-shank tools in collets. To use for high speed cutting and high precision milling.


Delivery:
With balanced clamping nut


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 