Morse taper adaptor SK 40 – 4 – 95

41.00

Application:
For mounting tools with Morse taper shank and tang according to DIN 228-1 form B.


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

ER-Precision collet ER40 | 472EP | < 5µm | O 7 - 6

37.00

Application:
For mounting straight-shank tools in collet chucks DIN 6499. To use for high speed cutting and high precision milling.


Note:
High flexibility: Large holding capacity up to –1 mm

ER-Collet chuck BT 40 – 1/10 – 100 | ER 16

63.00

Application:
For mounting straight-shank tools in collets.


Delivery:
With balanced clamping nut


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

End mill cutter 90° 25mm – 25mm Shank after DIN 1835B

143.00

  • For ISO Inserts APKT 1003... / APHX 1003...
  • With internal cooling
  • Nickel plated
  • Shank after DIN 1835B
  • Application in all materials
  • Delivery: without inserts

End mill holder Weldon with cooling channels SK 50 – 16 – 160

167.00

Application:
For mounting straight-shank tools with lateral flat according to DIN 1835 form B (Weldon).


Delivery:
With clamping screw and O-ring


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

OZ-Collet chuck SK 50 – 3/32 – 73 | OZ 32

113.00

Application:
For mounting straight-shank tools in collets.

Delivery:
With ball bearing clamping nut


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 

Boring bar blank HSK 100 – 97,5 – 250

238.00

Application:
For the manufacturing of special tools.


Note:
Cone and flange hardened and grinded. Soft body for later processing.


  • All holders are made of forged steel
  • Specific, low warpage hardened
  • Surface hardened HRC 58~60
  • Hardening depth 0,8mm~0,9mm
  • Taper angle tolerance < AT 3 according to DIN 2080
  • Surface roughness Ra < 0,4 µm
  • Tensile strength in the core of min. 800 N/mm? after DIN
  • All functional surfaces fine machined

 

 